    An investigation on the thermal and solar properties of graphene-coated polyester fabrics
    (MDPİ, 2021-02-01) Manasoglu, Gizem; MANASOĞLU, GİZEM; Celen, Rumeysa; ÇELEN, RUMEYSA; Kanik, Mehmet; KANIK, MEHMET; Ulcay, Yusuf; ULCAY, YUSUF; Bursa Uludağ Üniversitesi/Mühendislik Fakültesi/Tekstil Mühendisliği Bölümü.; 0000-0002-1504-8694; 0000-0002-2972-8295; JTS-3559-2023; AAI-8441-2021; AAI-8087-2021; IZE-4329-2023
    In this study, coatings were made with graphene nanopowder in two different thicknesses (0.1 and 0.5 mm) at three different concentrations (50, 100 and 150 g/kg) on polyester woven fabrics. The effects of the coating thickness and graphene concentration were examined with optical and scanning electron microscopy (SEM) images. The thermal stability properties of the samples were also evaluated by differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). Thermal conductivity was evaluated with two different principles: contact and radiant heat transfer, according to JIS R 2618 and EN ISO 6942, respectively. Solar measurements were performed with a Shimadzu UV-3600 Plus spectrophotometer. The graphene coating improved the thermal stability of the polyester fabrics. The solar absorbance value increased by 80% compared to reference fabrics, and reached approximately 90%. One of the important results was that the thermal conductivity coefficient increased by 87% and 262% for the two coating thicknesses, respectively.
  • Thumbnail Image
    Publication
    The effect of graphene coating on surface roughness and friction properties of polyester fabrics
    (Kaunas Univ Tech, 2021-01-01) Manasoglu, Gizem; Celen, Rumeysa; Akgün, Mine; Kanik, Mehmet; Manasoglu, Gizem; MANASOĞLU, GİZEM; Celen, Rumeysa; ÇELEN, RUMEYSA; Akgün, Mine; AKGÜN, MİNE; Kanik, Mehmet; KANIK, MEHMET; Bursa Uludağ Üniversitesi/Mühendislik Fakültesi/Tekstil Mühendisliği Bölümü.; 0000-0002-1504-8694; 0000-0002-2972-8295; JTS-3559-2023; JHT-0825-2023
    In this article, the surface roughness and friction coefficient values of graphene coated fabrics were examined. Fabrics were coated with three different graphene concentrations (5 %, 10 % and 20 %) with the knife-over-roll principle. The surface roughness of samples was measured by Accretech Surfcom 130A. Various surface roughness parameters of the coated fabrics were evaluated. Static and kinetic friction coefficients of coated fabrics were measured by Labthink Param MXD-02 friction tester using the standard wool abrasive cloth. It was observed that the coating concentration affected the frictional and roughness properties of fabrics. Experimental results showed that fabric surface roughness and friction coefficient values decreased significantly, especially at 20 % concentration. It was concluded that the coated fabrics produced could be used in applications such as anti-wear clothing.